Influence Of Porcelain Thickness And Repeated Firings On The Color Of Metal - Ceramic Restorations - An In Vitro Study
Influence of Porcelain Thickness & Repeated Firings On The Color Of Metal - Ceramic Restorations
DOI:
https://doi.org/10.70284/njirm.v7i4.1119Keywords:
Porcelain, Hue, Chroma, Lightness, Repeated firingAbstract
Background & Objectives: Color matching between ceramic restorations and natural teeth has been a major challenge in dentistry. Faults may occur during shade matching procedure in the dental clinic or in the laboratory at the time of fabrication of restoration. This study assessed the effect of porcelain thickness and repeated firing on the color of metal-ceramic restorations. Method: Thirty 12mm square samples of nickel chromium alloy were prepared and divided into three groups of 10 samples each. All samples were fired with opaque porcelain followed by dentin porcelain maintaining the dentin thickness to 1mm, 2mm and 3mm with silicon molds. The color of all the samples was measured with a spectrophotometer after 1st firing. Samples were subjected to repeated firing and color was again measured after 4th firing, 7th firing, 10th firing and 13th firing. The data was subjected to statistical analysis. Results: The results showed that increasing the thickness of porcelain resulted in significant increase in the Lightness (L*) and decrease in the Chroma (C*) of the samples. It also demonstrated that repeated firing did not cause significant color change (ΔE) on repeated firing of 1mm and 2mm, however, repeated firing of 3mm samples showed substantial color changes (ΔE) on repeated firing but this change was within acceptable limits of oral environment. Interpretation and Conclusion: The results of the study suggest that increased thickness of the dentin porcelain increases the Lightness (L*) thereby reducing the graying effect of the opaque layer. Therefore, maximum tooth reduction should be encouraged without violating the pulp integrity to provide enough space for the bulk of porcelain for better esthetic results. The results also show that repeated firing does not affect the color stability of the porcelain samples tested although significant color changes were seen with 3mm samples which were within acceptable limits of oral conditions. So, it can be inferred that repeated firing of the porcelain can be done to achieve correct contours and shape of the restorations. [Khanna T NJIRM 2016; 7(4): 132-139]
References
2. Douglas RD, Pryzybylaska M. Predicting porcelain thickness required for dental shade matches. J Prosthet Dent 1999;82:143-149.
3. Jorgenson MW, Goodkind RJ. Spectrophotometric study of five porcelain shades relative to the dimensions of color, porcelain thickness, and repeated firings. J Prosthet Dent 1979;42(1):96-105.
4. Barghi N. Color and glaze: Effects of repeated firings. J Prosthet Dent 1982;47(4):393-95.
5. O’Brien WM, Kay KS, Boenke KM, Groh CL. Sources of color variation on firing porcelain. Dent Mater 1991;7:170-173.
6. Barghi N, Lorenzana RE. Optimum thickness of opaque and body porcelain. J Prosthet Dent 1982;48(4):429-431.
7. Jacobs SH, Goodacre CJ, Moore BK, Dykema RW. Effect of porcelain thickness and type of metal ceramic alloy on color. J Prosthet Dent 1987;57(2):138-142.
8. Obregon A, Goodkind RJ, Schwabacher WB. Effects of opaque and porcelain surface texture on the color of ceramometals restorations. J Prosthet Dent 1981;46(3):330-340.
9. Groh CL, O’Brien WJ, Boenke KM. Differences in color between fired porcelain and shade guides. Int J Prosthodont 1992;5(6):510-514.
10. Fondriest J. Shade Matching in Restorative Dentistry: the Science and Strategies. Int J Periodont Rest Dent 2003;23(5):468-479.